Panda glass is more scratch resistant than Gorilla glass. This is because it has a higher hardness. Shatter Resistance. Panda glass is less likely to shatter than Gorilla glass. However, it is not completely shatterproof. If you drop your phone on a hard surface, there is a chance that the glass will break. In this test, a Knoop diamond is slowly forced along the glass surface to intentionally create scratches. The load, or pressure, of that diamond is also slowly increased. We look for a lateral crack to appear and then identify the load that caused the scratch. The higher the load, the more scratch resistant the glass. And the testing continues…. Oppo A53 Screen Scratch Test || Gorilla Glass 3NO any Scratch after Testing..on Display Bcoz Gorilla Glass Protectionnote:- it's Scratches Test not a Break Following that worrisome Samsung Galaxy Note 7 scratch test video, I spoke to Corning about Gorilla Glass 5's seemingly poor scratch resistant properties. So a Mohs pick of 3 cannot scratch Enter Victus, which promises double the scratch resistance of 2018’s Gorilla Glass 6. It performs better in a drop test, too, surviving a 2-meter fall compared to its predecessor’s 1.6m While it can survive 15 consecutive drops from 1 meter in test environments it is very different in the real world. There are so many other factors from a traditional drop that aren't tested for that it is hard to make an accurate claim. At the end of the day it's better to treat Gorilla glass as glass. About 72 hours after the video was uploaded online, Corning responded by implying that the test was conducted “in an uncontrolled manner.” Corning reps also stated that a 3 hardness pick can't scratch glass with a hardness of 5 or 6 like Gorilla Glass 5 has been proven to be (in lab tests). Corning uses the Knoop Diamond Scratch Test, where a diamond tip is drawn across the glass at a specific pressure level. Victus 2 increases the “scratch threshold” from 7-10 Newtons to 8-10 Newtons. It is also just slightly denser than original Victus, at 2.41g/cm3 from 2.40g/cm3 dYlQ.